Nitro-cellulose and alkyd resin based, air drying, single component, cellulosic based and filler varnish that fills the cavities and pores of wooden surfaces, is sanded easily and is used to prepare the surface for topcoat applications.
Cellulosic filler varnish is a filler varnish formulated to be successfully used on any wooden and parquet surfaces thanks to its fast drying and easy-to-sand structure and high filling capacity. It allows for unproblematic use of cellulosic polyurethane systems applied on top of it.
The product must be diluted down to desired viscosity with Yalaz cellulosic thinner by 25-30% and applied in 2 to 5 coats on the surface depending on the desired surface filling finish. Wait for 20-30 minutes in between the coats. The surface must be sanded 1.5-2 hours after application of the final coat. Cellulosic, polyurethane and polyester topcoat varnish should be applied having waited preferably overnight.
Dilution / Mixing Ratio
Diluted with cellulosic thinner by 90-100%.
1 kg of product covers a surface of 8-10 m2 in a single coat (with a dry film thickness of 35-40 µ).
(20°C)
Touch Dry: 10 minutes
Sanding Time: 1.5-2 hours
It can be stored for one year at a temperature of +5°C to +35°C in its original sealed packaging with no direct sunlight. Protect from extremely high temperatures and frost.
0.75 kg / 2.5 kg / 12 kg
Two-component, polyurethane based, reaction curing, topcoat varnish. Due to its polyurethane composition, it forms a physically hard film resistant to scratches and impacts and to discoloration. It creates a plump film coat due to its high solid mate
Acrylic, copolymer resin based, silicone modified, transparent varnish resistant to impacts, friction, weak acids and alkaline solutions.
Alkyd binder based, air drying, glossy topcoat paint with superior properties.
Synthetic alkyd resin based, antirust primer with adherence and durability and high hide, which is used under topcoat paints to prevent rusting of interior and exterior iron and iron-derivative metal surfaces due to corrosive effects in the atmospher
Alkyd and nitro-cellulose based, high hide, fast drying, metallic, glossy topcoat paint with high physical and chemical resistance, and superior elasticity and glossiness.
Chlorinated rubber modified alkyd resin based, fast drying paint.
Water-based, pure acrylic resin based, odorless and decorative interior wall paint that looks glittery and nacreous when the light hits on the surface.
Nacreous, durable, scrubbable and washable, easy-to-apply and environment friendly decorative topcoat that creates attractive, decorative effects on walls.