2k Acrylic Topcoat

PROPERTIES

• Excellent elasticity, physical and chemical properties.
• High resistance to ultraviolet rays.
• High gloss permanence.
• Excellent adhesion.
• Fast drying.

APPLICATION SURFACES

It is used as topcoat in particularly outdoor areas for protection of steel and other metal surfaces intended to be resistant to UV rays and in general industry, by machine manufacturers, for metal protection and for painting of steel constructions.

APPLICATION METHOD

2 parts of Component A and 1 part of Component B are mixed. The two components are provided in two separate containers at the specified mixing ratio. The entire amounts of the two components must be mixed. The mixture must be stirred with a mechanical stirrer, the hardener must be added slowly when stirring the main material and stirring should be continued for 5-10 minutes. After stirring is done, the mixture must be left to rest for 20-30 minutes. The viscosity of application is adjusted with Yalaz Acrylic Thinner by 10-15% at 16 to 22 sec (20°C DIN CUP4), and the paint is applied in 2-3 coats. The mixture prepared for application must be used and finished in 5-7 hours. The paint should be applied as a powder on the surface of application first and then applied in the desired thickness.

Dilution / Mixing Ratio

Paint: 2 parts

Hardener: 1 part

Thinner: 10-15%

Paintable (Coverable) Area

Paints a surface of 14-16 m2/liter in a single coat. (for applications of paint + hardener in film thickness of 40 microns).

Drying Time

(20°C):

At a temperature of 20°C and relative humidity of 50%, it dries to the touch in 1-2 hours and hard dries in 10 - 12 hours. It becomes resistant to chemicals in 5-7 days.

Storage

It must be kept and stored in a cool and dry environment with no direct sunlight. It can be stored in its original packaging for minimum 1 year. Keep the lid closed after using. Protect from frost.

Packaging

15 kg of Component A + 7.5 kg of Component B: a Set of 22.5 Kg